Analisis Serbuk Silika Amorf (SiO2) Berbahan Dasar Pasir

  • Stevi Silahooy Universitas Pattimura
Keywords: hydrothermal-coprecipitation; sand; amorphous silica powder (SiO2)

Abstract

The aim of the research was to synthesize amorphous silica powder (SiO2) made from sand obtained from the Bancar-Tuban area using the hydrothermal-coprecipitation method using 7M NaOH as solvent. The samples obtained were characterized using X-Ray Fluorescence (XRF), X-Ray Diffraction (XRD), and Scanning Electron Microscopy (SEM). The characterization results show that there has been an increase in the percentage of weight (wt%) Si from 71.5% to 92.20%. The structure of the silica formed is a with non-uniform particle size with an average size exceeding ≥110.09 nm. The results of observations using SEM instruments that were carried out using various variations showed that the SiO2 particle size was not uniform, where the SiO2 powder tended to agglomerate

Downloads

Download data is not yet available.

References

Aristia, G.A. (2014), Sifat Korosi Komposit PANi/SiO2 Bervariasi Struktur Pada Larutan Salinitas Tinggi. Tesis. Jurusan Fisika. FMIPA, Institut Teknologi Sepuluh Nopember Surabaya.
Munasir, Triwikantoro, Zainuri, M, Darminto, (2012), “Uji XRD dan XRF pada bahan mineral (Batuan dan Pasir) Sebagai Sumber Material Cerdas (CaCO3 dan SiO2)’’, Jurnal Penelitian Fisika Dan Aplikasinya (JPFA), Vol 2 (1), hal. 20-29.
Munasir, Sulton, A., Triwikantoro, Zainuri, M., Darminto. (2013), “Synthesis of Silica Nanopowder Produced fromIndonesian Natural Sand via Alkalifussion Route”, The 2nd International Conference on Theoretical and Applied Physics, American Institute of Physics, Palangkaraya, hal. 28-31.
Samsudin, A., Heru, S., Sugeng, W., Agus, P., Ratna, B., Adv. Pow. Tech 20 : 468-472 (2009).
S. Hadi, Munasir, and Triwikantoro, “Sintesis Silika Berbasis Pasir Alam Bancar Menggunakan Metode Kopresipitasi.”
Scha ̈ ́f, O, Ghobarkar, H, Knauth, P. (2004), “Hidrothermal Synthesis of Nanomaterials”, in: Knauth, P., Schoonman, J. 9Eds.), Nanostructured Materials, electronic Materials: Science & Technology. Springer US, hal. 23-41.
Ummah, H., dan Munasir., (2015), “Studi Sifat Anti-Korosi Material Coating Cat-PANi/SiO2 dengan Metode Polarisasi Linear”, Jurnal Inovasi Fisika Indonesia, Vol 04, No 03, hal 133-137.
Zuhri, A. Arifudin. 2013. “Sintesis dan Karakterisasi Nanokomposit PANi/SiO2 Sebagai Pelapis Anti Korosi”, Jurnal Inovasi Fisika Indonesia, Vol .02, No 03, hal. 1-6.
Published
2020-11-24
How to Cite
SilahooyS. (2020). Analisis Serbuk Silika Amorf (SiO2) Berbahan Dasar Pasir. Science Map Journal, 2(2), 75-78. https://doi.org/10.30598/jmsvol2issue2pp75-78