Analisa Keragaman Nilai Kekerasan Baja St-42 Melalui Proses Karburasi Menggunakan Komposisi BaCO3 Dan Carbon Dengan Variasi Waktu Penahanan
Abstract
Pack carburizing is a method of thermo chemical treatment, when carbon dissolved in steel surfaces, revolve 0.3% - 0.9% with temperature between 825 oC - 925 oC, and keep it at several time and then continued with quenching process using water, oil, air or salt. This research had arranged to test the hardness of low carbon steel (ST-42) with 40% of BaCO3, and 60% of Carbon, before and after carburizing process in 3 type of holding time: 15, 30, and 50 minutes. Based on results, the best combination to reach a higher value of hardness provides by combination of after carburizing process and 50 minutes of holding time. Later, an extensive experiment by 2 hours of burning had shown an increase level of hardness up to 365% from the initial condition which proves the quality of this best treatment combination.
Downloads
An author who publishes in the ARIKA Jurnal agrees to the following terms:
- The author retains the copyright and grants ARIKA journal the right of first publication of the work simultaneously licensed under the Creative Commons Attribution-ShareAlike 4.0 License that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal.
- The author is able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book) with the acknowledgment of its initial publication in this journal.
- The author is permitted and encouraged to post his/her work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of the published work (See The Effect of Open Access).